The crack growth test results undergoing thermomechanical fatigue showed that the life of TMF specimens with notched laser drilled holes exhibit a debit by as much as 4 times that of smooth gage section specimens under the same loading conditions. Such a significant change in number of cycles to failure must be accounted in any damage tolerant design system. The detailed fractographic analysis demonstrated that the all cracks start crystallographically ...