Abstract:
Fiber/matrix interfacial debonding and frictional sliding stresses were evaluated by single-fiber pushout tests on unidirectional continuous silicon-carbide-fiber-reinforced, reaction-bonded silicon nitride matrix composites. The debonding and maximum pushout loads required to overcome interfacial friction were obtained from load-displacement plots of pushout tests. Interfacial debonding and frictional sliding stresses were evaluated for composites with various fiber contents and fiber surface conditions (coated and uncoated), and after matrix densification by hot isostatic pressing (HIPing). For as-fabricated composites, both debonding and frictional sliding stresses decreased with increasing fiber content. The HIPed composites, however, exhibited higher interfacial debonding and frictional sliding stresses than those of the as-fabricated composites. These results were related to variations in axial and transverse residual stresses on fibers in the composites. A shear-lag model developed for a partially debonded composite, including full residual stress field, was employed to analyze the nonlinear dependence of maximum pushout load on embedded fiber length for as-fabricated and HIPed composites. Interfacial friction coefficients of 0.1-0.16 fitted the experimental data well. The extremely high debonding stress observed in uncoated fibers is believed to be due to strong chemical bonding between fiber and matrix.
| Description: |
Journal article |
| Pages: |
8 |
| Report Date: |
1994 |
| Contract Number: |
W31109Eng38 |
| Report Number: |
D860852 |
Report Unavailable |
| This title is unavailable from Storming Media. We do not know when it might be available, if at all. We list the report on our site for bibliographic completeness, to help our users know what other work has been performed in this field. Please note that as with all titles on this site, we do not have contact information for any of the authors. Nor can we give any suggestions on how one might obtain this report. |
|
|
|
Email This Abstract