A study of morphology of simple oxidation and hot corrosion of the aligned Co-10 wt.% Cr-14 wt.% TaC alloy was performed at 900 C in still air. The morphology of simple oxidation was found to correlate well with previous results on similar alloys. Hot corrosion tests were performed by coating the samples with a thin layer of Na(sub 2)SO(sub 4) and exposing them to still air at 900 C. A radically different morphology was found and extensively analyzed using optical microscopy and the electron microprobe. These results are then explained using a localized reduction model of hot corrosion.
Pages:
18
Report Date:
DEC 80
Report Number:
D473021
Report Unavailable
This title is unavailable from Storming Media. We do not know when it might be available, if at all. We list the report on our site for bibliographic completeness, to help our users know what other work has been performed in this field. Please note that as with all titles on this site, we do not have contact information for any of the authors. Nor can we give any suggestions on how one might obtain this report.
Email This Abstract